Bids Are Invited For BEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END: ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 33 DEG RADIUS : 1490 MM WALL THICKNESS : MINIMUM 6 MM SIZE : 400 NB ADDITIONAL INFORMATION : 9578/KGN/FES/M/2024/217/27 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) PAINTING SCHEDULE: A)SURFACE PREPARATION-POWER TOOL CLEANING. B)PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS: 5493,:25-40 MICRONS (DFT). D)FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE: RAL 9002, GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS: 5493:25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 2 100246616 - 20 - M1774990597 - BEND: CB-L,FLG,35D,R1360MM,6MM,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END: ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 35 DEG RADIUS : 1360 MM WALL THICKNESS : MINIMUM 6 MM SIZE : 400 NB ADDITIONAL INFORMATION : 9578/KGN/FES/M/2024/217/27 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) PAINTING SCHEDULE: A)SURFACE PREPARATION-POWER TOOL CLEANING. B)PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS: 5493,:25-40 MICRONS (DFT). D)FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE: RAL 9002, GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS: 5493:25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 3 100246616 - 30 - M1774990596 - BEND: CB-L,FLG,20D,R2700MM,6MM,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END:ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 20 DEG RADIUS : 2700 MM WALL THICKNESS : MINIMUM 6 MM SIZE : 400 NB ADDITIONAL INFORMATION : 9578/KGN/FES/M/2024/217/27 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) PAINTING SCHEDULE: A)SURFACE PREPARATION-POWER TOOL CLEANING. B)PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS: 5493,:25-40 MICRONS (DFT). D)FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE: RAL 9002, GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS: 5493:25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 4 100246616 - 40 - M1774990599 - BEND: CB-L,FLG,30D,R1644MM,6MM,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END:ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 30 DEG RADIUS : 1644 MM WALL THICKNESS : MINIMUM 6 MM SIZE : 400 NB ADDITIONAL INFORMATION : 9578/KGN/FES/M/2024/217/27 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) PAINTING SCHEDULE: A)SURFACE PREPARATION-POWER TOOL CLEANING. B)PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS: 5493,:25-40 MICRONS (DFT). D)FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE: RAL 9002, GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS: 5493:25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 5 100246616 - 50 - M1774990594 - BEND: CB-L,FLG,IS3589,24D,R2188,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 3589 ANGLE : 24 DEG RADIUS : R2188 SIZE : 400 NB ADDITIONAL INFORMATION : DRG NO:9578/KGN/FES/M/2024/217/27 1) BASALT PROPERTIES:COMPRESSIVE STRENGTH:4500 KG/SQCM (MIN),DENSITY:2.8 TO 3.1 GM/CM3,HARDNESS OF BASALT LINING:8 MHOS (MIN) BENDING STRENGTH:300 KG/SQCM (MIN),WATER ABSORPTION:0.5 % (MAX) 2) PAINTING SCHEDULE:A) SURFACE PREPARATION-POWER TOOL CLEANING. B) PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C) UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS:5493,25-40 MICRONS (DFT) D) FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE:RAL 9002,GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493,25-40 MICRONS (DFT) 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062 6) THICKNESS:MIN 6 MM,MORTAR THICKNESS:9 MM,MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION:A) SIO2:42-54% B) AL2O3:8-19% C)CAO + MGO:11-22% D) FE2O3 + FEO:11-25% Schedule No. 6 100246616 - 60 - M1774990593 - BEND: CB-L,FLG,IS3589,21D,R2507,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 3589 ANGLE : 21 DEG RADIUS : R 2507 SIZE : 400 NB ADDITIONAL INFORMATION : DRG NO:9578/KGN/FES/M/2024/217/27 1) BASALT PROPERTIES:COMPRESSIVE STRENGTH:4500 KG/SQCM (MIN),DENSITY:2.8 TO 3.1 GM/CM3,HARDNESS OF BASALT LINING:8 MHOS (MIN),BENDING STRENGTH:300 KG/SQCM (MIN),WATER ABSORPTION:0.5% (MAX) 2) PAINTING SCHEDULE:A) SURFACE PREPARATION-POWER TOOL CLEANING. B) PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C) UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS:5493,25-40 MICRONS (DFT) D) FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE:RAL 9002,GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493,25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062 6) THICKNESS:6 MM,MORTAR THICKNESS:9 MM,MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM) 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION:A) SIO2:42-54% B) AL2O3:8-19% C) CAO + MGO: 11-22% D) FE2O3 + FEO:11-25% Schedule No. 7 100246616 - 70 - M1774990595 - BEND: CB-L,FLG,IS3589,32D,R1566,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 3589 ANGLE : 32 DEG RADIUS : R1566 SIZE : 400NB ADDITIONAL INFORMATION : DRG NO:9578/KGN/FES/M/2024/217/27 1) BASALT PROPERTIES:COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN),DENSITY:2.8 TO 3.1 GM/CM3,HARDNESS OF BASALT LINING:8 MHOS (MIN),BENDING STRENGTH:300 KG/SQCM (MIN),WATER ABSORPTION:0.5% (MAX) 2) PAINTING SCHEDULE:A) SURFACE PREPARATION-POWER TOOL CLEANING. B) PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS:5493,25-40 MICRONS (DFT). D) FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE:RAL 9002,GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493,25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) THICKNESS:MIN 6 MM,MORTAR THICKNESS:9 MM,MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM) 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION:A) SIO2:42-54% B) AL2O3:8-19% C)CAO + MGO:11-22% D) FE2O3 + FEO:11-25% Schedule No. 8 100246616 - 80 - M1735995691 - TEE: CB-L,FLG,MS,IS2062,6MM,400NB Technical SpecificationsTEE,PIPE TYPE : CAST BASALT LINED END CONNECTION : TEE END:FIXED FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 WALL THICKNESS : MINIMUM 6 MM SIZE : 400 NB ADDITIONAL INFORMATION : 9578/KGN/FES/M/2024/217/28 & 1 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) PAINTING SCHEDULE: A)SURFACE PREPARATION-POWER TOOL CLEANING. B)PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS: 5493,:25-40 MICRONS (DFT). D)FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE: RAL 9002, GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS: 5493:25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 9 100246616 - 90 - M1774990602 - BEND: CB-L,FLG,45D,R1200,6MM,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END:ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 45 DEG RADIUS : 1200 MM WALL THICKNESS : MINIMUM 6 MM THICK SIZE : 400 NB ADDITIONAL INFORMATION : DRAWING:9578/KGN/FES/M/2024/217/28 & 3 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) PAINTING SCHEDULE: A)SURFACE PREPARATION-POWER TOOL CLEANING. B)PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS: 5493,:25-40 MICRONS (DFT). D)FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE: RAL 9002, GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS: 5493:25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 10 100246616 - 100 - M1774990603 - BEND: CB-L,FLG,45D,R1200,6MM,400NB Technical SpecificationsBEND,PIPE TYPE : CAST BASALT LINED END CONNECTION : BOTH END:ROTATING FLANGES MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 45 DEG RADIUS : 1200 MM WALL THICKNESS : MINIMUM 6 MM SIZE : 400 NB ADDITIONAL INFORMATION : 9578/KGN/FES/M/2024/217/28 & 2 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) PAINTING SCHEDULE: A)SURFACE PREPARATION-POWER TOOL CLEANING. B)PRIMER-2 COATS OF ZINC PHOSPHATE [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS:5493]< 35-40 MICRONS (DFT) EACH. C)UNDER COAT-ONE COAT OF COLOURED PIGMENTS (FULL COLOURS) SUITABLY EXTENDED DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN CONFORMING TO BS: 5493,:25-40 MICRONS (DFT). D)FINISH COAT-ONE COAT OF FADE RESISTANT COLOURED PIGMENTS SHADE: RAL 9002, GREY [DRYING OIL MODIFIED WITH PHENOLIC OR PHENOLIC MODIFIED RESIN] CONFORMING TO BS: 5493:25-40 MICRONS (DFT). 3) SUITABLE MS LIFTING LUG TO BE PROVIDED 4) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 5) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 6) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 7) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 11 100246616 - 110 - M1774990601 - LATERAL,CB-L,FLG,MS,45D,5MM,200NB Technical SpecificationsFITTING,PIPE ITEM DESCRIPTION : LATERAL TYPE : CAST BASALT LINED END CONNECTION : FLANGED MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 45 DEG THICKNESS : MINIMUM 5MM THIICK NOMINAL SIZE : 200 NB DRAWING NUMBER:KGN-AHP-PCL-45 LATERAL 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN), DENSITY:2.8 TO 3.1 GM/CM3, HARDNESS OF BASALT LINING:8 MHOS (MIN), BENDING STRENGTH:300 KG/SQCM (MIN), WATER ABSORPTION: 0.5% (MAX) 2) SUITABLE MS LIFTING LUG TO BE PROVIDED 3)MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 4)FLANGES/COLLAR MATERIAL:AS PER IS 2062. 5) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 6) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25%. Schedule No. 12 100246616 - 120 - M1774990600 - LATERAL,CB-L,FLG,MS,45D,5MM,250NB Technical SpecificationsFITTING,PIPE ITEM DESCRIPTION : LATERAL TYPE : CAST BASALT LINED END CONNECTION : FLANGED MATERIAL : MILD STEEL MATERIAL SPEC : IS 2062 ANGLE : 45 DEG THICKNESS : MINIMUM 5MM THIICK NOMINAL SIZE : 250 NB DRAWING NUMBER:KGN-AHP-PCL-45% LATERAL 1) BASALT PROPERTIES: COMPRESSIVE STRENGTH:4500 KG/SQCM(MIN),DENSITY:2.8 TO 3.1 GM/CM3,HARDNESS OF BASALT LINING:8 MHOS (MIN),BENDING STRENGTH:300 KG/SQCM (MIN),WATER ABSORPTION: 0.5% (MAX) 2) SUITABLE MS LIFTING LUG TO BE PROVIDED 3) MS CASING PIPE MATERIAL CONFIRMING TO IS-2062 AND TOLERANCES AS PER IS 3589. 4) FLANGES/COLLAR MATERIAL:AS PER IS 2062. 5) MORTAR THICKNESS:9MM, MINIMUM BASALT THICKNESS:20 MM (+/- 2 MM). 6) CAST BASALT INDICATIVE CHEMICAL COMPOSITION: A) SIO2:42-54% B) AL2O3: 8-19% C)CAO + MGO: 11-22% D) FE2O3 + FEO: 11-25% otal Quantity : 97
