Bids Are invited for 71510200080700 - Brick,Ls-1,Dwn:3.32.32.55.60.V/72989 - Brick,Ls-1,Dwn:3.32.32.55.60.V/72989 Unit Weight:15.8Kg,Quality:60%Al2o3,Fe203 1.5%Maximum Pce Oc 36Minimum,Rul 1560Deg C Minimum Plc At 1500Deg C/2 Hrs +/-0.5% Maximum Spalling Resistance In Air +30 Cycles Bd 2.4Gms/Cc Min Ap 16% Maximum For Press 20% Maximum F Or Hand Moulding Ccs 600Kg/Cm2 Minimum For Press 400Kg/Sqcm Minimum For H/Moulding St +/-1% Or +/-2Mm Whichever Is Greater Drawing No : 3.32.32.55.60.V/72989 , 71510200080767 - Brick,Shape La-1,Ut Wt:22Kg - Brick,Shape La-1,Ut Wt:22Kg For Nlcp,Alumina 60%Minimum,Fe2o3 1.5% Maximum,Pce Oc 36 Minimum Rul 1560Deg C Minimum Plc At 1500Deg C/2 Hrs And-0.5% Maximum Spalling Resistance In Air And 30 Cycles Bd 2.4Gms/Cc Minimum Ap-16% Maximum For Press 20% Maximum For H/Mo Ulding Ccs 600Kg/Cm2 Min For Press 400Kg/Cm2 Minimum For H/Moulding St +/-1% Or +/-2Mm Whichever Is Greater Drawing No : 3.32.55.60.V/72989 , 71510200080691 - Brick,Fire,Shape B-6,Nlcp,Ut Wt:47.00Kg - Brick,Fire,Shape B-6,Nlcp,Ut Wt:47.00Kg Quality:60% Al2o3 Drawing No : 33.255.60.91.6010 R1 , 71510200083207 - Brick,Fire,Shape B11,60%Alumina - Brick,Fire,Shape B11,60%Alumina For Nlcp, Unit Weight: 55.28 Kgs, Quality: 60% Alumina, Chemical Prop.: Al2o3(%): 60 Min., Fe2o3(%): 1.5 Max., Physical Prop.: Pce (Orton): 36 Min., Rul(Ta Deg C):1560 Min., Plcar At 1500 Deg C For 2 Hrs: +/- 0.5% Max., Spalling(Cycl Es): +30, B.D. Min.: 2.4 Gm/Cc, Ap(%) Maximum: 16 For Press & 20 For H/M, Ccs (Kg/Cm2) Min.: 600 For Press & 400 For H/M, Size Toler Ance: +/-1% Or +/- 2Mm Whichever Is Greater. Drawing No : 3325560916011R02 , 71510200083208 - Brick,Fire,Shape B12,60%Alumina - Brick,Fire,Shape B12,60%Alumina For Nlcp, Unit Weight: 46.33 Kgs, Quality: 60% Alumina, Chemical Prop.: Al2o3(%): 60 Min., Fe2o3(%): 1.5 Max., Physical Prop.: Pce (Orton): 36 Min., Rul(Ta Deg C):1560 Min., Plcar At 1500 Deg C For 2 Hrs: +/- 0.5% Max., Spalling(Cycl Es): +30, B.D. Min.: 2.4 Gm/Cc, Ap(%) Maximum: 16 F