Bids Are invited for 71510200083723 - Brick, 60%Al2o3, Shape: G32, Uw: 9.30Kg - Brick, 60%Al2o3, Shape: G32, Uw: 9.30Kg Brick, Fire, 60% Alumina, Shape: G32, Unit Weight: 9.30 Kg, Specification: Al2o3: 60% Min, F E2o3: 1.50% Max., Pce: 36 Orton Min., Rul (Ta Value): 1560 °C. Min, Plc At 1500 °C. / 2 Hrs: +/- 0.5% Max, Spalling: 30 Cycles Min, Bulk Density: 2.40 Gm/Cc Min, Apparent Porosity: 16% Max. (Press) & 20% Max (Hand Moulding), Ccs: 600 Kg/Sq. Cm Min. (Press) & 400 K G/Sq. Cm Min. (Hand Moulding), Size Tolerance: +/-1% Or +/- 2Mm Whichever Is Greater, Ref. Drg. No. Dsp/Qualical/05/ 13/01/Bof-Expn- 14Rt/Be/07638 Rev-0 , 71510200083724 - Brick, 60%Al2o3, Shape: G52, Uw:9.10Kg - Brick, 60%Al2o3, Shape: G52, Uw:9.10Kg Brick, Fire, 60% Alumina, Shape: G52, Unit Weight: 9.10 Kg, Specification: Al2o3: 60% Min, Fe 2O3: 1.50% Max., Pce: 36 Orton Min., Rul (Ta Value): 1560 °C. Min, Plc At 1500 °C. / 2 Hrs: +/- 0.5% Max, Spalling: 30 Cycles Min, B Ulk Density: 2.40 Gm/Cc Min, Apparent Porosity: 16% Max. (Press) & 20% Max (Hand Moulding), Ccs: 600 Kg/Sq. Cm Min. (Press) & 400 Kg /Sq. Cm Min. (Hand Moulding), Size Tolerance: +/-1% Or +/- 2Mm Whichever Is Greater, Ref. Drg. No. Dsp/Qualical/05/ 13/01/Bof-Expn-1 4Rt/Be/07637 Rev-0 , 71510200083725 - Brick, 60%Al2o3, Shape: Gb32, Uw:14 Kg - Brick, 60%Al2o3, Shape: Gb32, Uw:14 Kg Brick, Fire, 60% Alumina, Shape: Gb32, Unit Weight: 14.00 Kg, Specification: Al2o3: 60% Min, Fe2o3: 1.50% Max., Pce: 36 Orton Min., Rul (Ta Value): 1560 °C. Min, Plc At 1500 °C. / 2 Hrs: +/- 0.5% Max, Spalling: 30 Cycles Min,Bulk Density: 2.40 Gm/Cc Min, Apparent Porosity: 16% Max. (Press) & 20% Max (Hand Moulding), Ccs: 600 Kg/Sq. Cm Min. (Press) & 400 Kg/Sq. Cm Min. (Hand Moulding), Size Tolerance: +/-1% Or +/- 2Mm Whichever Is Greater, Ref. Drg. No. Dsp/Qualical/05/ 13/01/Bof-Expn -14Rt/Be/07642 Rev-0 , 71510200083726 - Brick,60%Al2o3, Shape: Gb52, Uw:13.70Kg - Brick,60%Al2o3, Shape: Gb52, Uw:13.70Kg Brick, Fire, 60% Alumina, Shape: Gb52, Unit Weig